Zinc chromium chromate pigment

ABSTRACT

Zinc oxide is interacted with an aqueous solution containing a chromium chromate complex obtained through partial reduction of an aqueous solution of chromic acid with an organic reducing agent. The resulting product is dried and the residual solid ground to suitable size for use as a pigment.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates generally to the field of corrosion-inhibiting pigments and is particularly concerned with such pigments comprising both zinc and chromium in chemical combination.

2. Prior Art

Metal protective pigments have long been used as components of coating compositions applied to metallic surfaces. Certain of these pigments have been, at least partially, effective in providing a specific inhibiting or passivating action at the surface of the metal. Among the useful pigments in this category are red lead and certain chromium containing pigments.

Among the better known chromium-containing pigments suggested for use in metal protecting coatings are zinc yellow or so called "zinc chromate" and zinc tetroxy chromate. These, among other pigments, are described in Kirk-Othmer: Encyclopedia of Chemical Technology, 2d. ed., Vol. 5 at pages 507-510; and by V. H. Chalupski in the monograph appearing in UDY: Chemistry of Chromium and its Compounds, Vol. 1 (Rheinhold Publishing Co., 1956) beginning at Page 357, particularly at pages 375-381. A further modified method for preparing zinc yellow is described in U.S. Pat. No. 2,410,916.

Zinc chromates have been used for many years as corrosion-inhibitive pigments. These pigments are used in formulations of paint and coating systems to protect metals against corrosion. The zinc chromate pigment may be used with other pigments such as red lead and ferric oxide pigments and/or with pigment extenders which may be applied as metal primers, such as, for example, in structural steel priming, on ships, aircraft, automotive bodies, etc.

The "zinc chromate" in present commercial use, or zinc yellow pigment as it is referred to in the trade, is a basic potassium zinc chromate, stated to have the empirical formula 4ZnO.4CrO₃. K₂ O.3H₂ O. It can be made by a variety of processes, all based on the reaction of zinc and chromate compounds in aqueous solution and in the presence of potassium salts. Thus, it may be prepared by the reaction of acidified zinc oxide with potassium dichromate. The procedure described in U.S. Pat. No. 2,410,916 involves precipitation of a zinc salt with a solution of a chromate in the presence of potassium ions and hydroxyl ions. Other procedures described in the literature include initial treatment of the zinc oxide with KOH to render it reactive, followed by addition of the chromate solution in the form of potassium tetrachromate, (Kirk-Othmer, op. cit., Vol. V, pages 509-510).

Another commercial process involves the dispersion of zinc oxide in water, adding thereto a solution of potassium dichromate following by hydrochloric acid. The reaction may be expressed by the following equation:

    4ZnO+2K.sub.2 Cr.sub.2 O.sub.7 +2HCl→4ZnO. 4CrO.sub.3.K.sub.2 O. 3H.sub.2 O+2KCl

Among other chromium pigments asserted to possess corrosion inhibitive properties are included chromates of alkaline earth metals and respectively of lead and iron, which pigments may also include alkali metal cation (potassium). A number of these have been exploited commercially to some extent.

In U.S. Pat. No. 2,387,528 there are described alkaline earth metal chromates containing trivalent as well as hexavalent chromium, such as basic calcium chromito-chromate. These pigments, because of various drawbacks, have not attained commercial significance; UDY: op. cit. at page 381; Kirk-Othmer, op. cit. at page 510. These are prepared, according to the patent, by roasting a mixture of the alkaline earth metal chromate and an alkaline earth metal compound which is heat decomposable to the oxide, in designated proportions and grinding the resulting product.

Solutions of chromates have also been applied to metal surfaces or to "conversion coatings" on such metals to improve corrosion resistance and paint bonding characteristics. Thus, U.S. Pat. No. 2,902,394 describes metal protecting compositions for application to zinc surfaces, prepared by intimate admixture of chromic acid with aqueous nitric, sulfuric and acetic acids and with a sulfite-type reducing agent capable of reducing a minor portion of the hexavalent chromium to trivalent state.

An earlier patent of the present inventor, U.S. Pat. No. 3,063,877, describes aqueous solutions for treating metal surfaces to impart improved corrosion resistance, which solutions are prepared by partially reducing a dissolved hexavalent chromium compound with formaldehyde, under conditions such that at least 5% and preferably at least 20% of the total chromium is present in reduced state.

U.S. Pat. No. 3,279,958 describes rinsing of phosphate, chromate, and other chemical conversion coatings on metal surfaces with a dilute aqueous acidic solution of a chromium chromate complex, followed by a water rinse. The complex is prepared by treating aqueous chromic acid solution with an organic reducing agent which contains an active hydroxyl, aldehyde or carboxyl group, to reduce a portion of the hexavalent chromium to the trivalent state.

SUMMARY OF THE INVENTION

In accordance with the present invention, novel corrosion-inhibiting pigments are provided which comprise a complex of zinc associated with chromium, wherein the chromium is present in both trivalent and hexavalent state.

The novel pigments of the invention are produced by interaction of zinc oxide with a solution of a chromium chromate complex prepared by partial reduction of an aqueous solution of chromium trioxide with a soluble organic oxidizable compound containing an active hydroxyl, aldehyde or carboxyl group, followed by drying and grinding to desired pigment size particles.

The pigments thus obtained, when applied in conventional vehicles for coating metal surfaces, have a passivating effect on such surfaces and impart pronounced capacity for resisting corrosion.

DETAILED DESCRIPTION

A wide selection of oxidizable organic compounds is applicable for partial reduction of the chromic acid; e.g. formaldehyde, methanol, ethanol, citric acid, sucrose, furfural, etc. From the standpoint of convenience, economy, and performance, the preferred reducing agents are methanol, formaldehyde and furfural.

In a preferred procedure, the zinc oxide is dispersed in water or is made into an aqueous paste. A solution containing the chromium chromate complex is then added to the zinc oxide dispersion or paste, slowly while stirring.

Since neither alkali metal salts nor other extraneous substances are employed in making the pigment of the invention, expensive purification steps, which otherwise would be required to free the pigment of by-products and particularly of deleterious by-products, is avoided. The obtained zinc chromium chromate pigment is free of extraneous metal ions and does not contain chloride, sulfate or other acidic anions that may be deleterious to the corrosion inhibiting properties of the pigment.

The relative content of zinc and chromium in the pigment will, of course, depend upon the proportions of these in the reacting mixture. The ratio of trivalent to hexavalent chromium in the pigment will be substantially that of the chromium chromate complex in the solution reacted. The empirical formula of the obtained pigment can be expressed by the formula:

    xZnO.yCrO.sub.3.zCr.sub.2 O.sub.3

The mol ratio of x:(y+z) may be in the range of 5:1 to 1:3. Of the total chrome content of the pigment, 5 to 70% and preferably 25 to 65% should be present in the reduced state (Cr^(III)). The pigment may also contain associated water, depending upon conditions of preparation.

Th primary purpose of the zinc chromate pigment thus produced is not as a colorant but as a material which provides useful corrosion-inhibiting action when incorporated in paints and coating compositions applied to metal surfaces.

The chromium chromate solution may be prepared by methods described in U.S. Pat. No. 3,063,877 or by the methods described in my companion application Ser. No. 883,507 for CORROSION INHIBITIVE PIGMENT, filed Mar. 6, 1978. For example, a 20 to 50% by weight aqueous solution of chromic acid is reacted with the desired organic reducing agent of the type described employing less than 1 mol reductant per mol of chromium compound, to assure only partial reduction of the latter.

In a preferred procedure, a 33% by weight aqueous solution of chromic acid is employed, to which the selected reducing agent is added with vigorous stirring, using one mol of the reducing agent for 3 mols of chromic acid. The reaction is highly exothermic and slow addition of the reductant with vigorous stirring is necessary during the entire period of addition to permit close control of temperature and reaction rate. The temperature should be kept below 95° C., preferably below 85° C. When addition of reductant has been completed, stirring is continued until no further reaction is evident (by gas evolution). The obtained solution, as such, may be reacted with zinc oxide, if desired, with adjustment of water content to preferred extent in the reaction mixture.

EXAMPLE 1 Solution A

150 pounds (68.04 kg.) of chromium trioxide are dissolved in 40 gallons (151.4 liters) of water. 42 pounds (19.05 kg.) of commercial formalin (36.6%) dissolved in 18 gallons (68.1 liters) of water, are added to the chromium trioxide solution, slowly with stirring. The addition rate is controlled to maintain the reaction temperature below 85° C. When the reaction subsides, water is added to make a total of 100 gallons (378.5 liters) of concentrate. This concentrate contains 1.5 pounds of total chromium oxides per gallon (180 gm/liter) with in the order of about 42% of the total chromium being present in reduced state.

Slurry B

122 pounds (55.3 kg.) of zinc oxide are dispersed in 32 gallons (121 liters) of water to form a slurry.

Pigment preparation

Solution A is added slowly with vigorous stirring into Slurry B and the mixture agitated for 4 hours with heating at a temperature of 120°-125° C. to remove excess water. The obtained product is then further dried in an oven at about 175° C., and subsequently ground in a pebble mill to pigment size. The pigment will contain zinc to total chromium in about equal molar amounts.

The novel dry pigments of the invention may be used alone or together with other pigments in paints and coating compositions in the same manner as the already known commercial chromium-containing corrosive-inhibiting pigments such as, for example, zinc yellow, zinc tetroxychromate (4ZnO.ZnCrO₄.xH₂ O). Pigment E (barium potassium chromate), Pigment M-50 (composite of basic lead chromate coated onto a lead silicate-silica base). These known corrosion inhibiting pigments are conventionally made up into metal coating and painting compositions with typical oleoresinous vehicles such as drying and semi-drying oils or with certain latex emulsions including synthetic resin polymers. The pigments of the present invention may be used in like manner. 

What is claimed:
 1. A zinc chromium chromate corrosion inhibiting pigment wherein the mol ratio of zinc oxide to total chromium oxides is about in the range of 5:1 to 1:3 and 5 to 70% of the total chromium content is present in trivalent state.
 2. A zinc chromium chromate corrosion inhibiting pigment as defined in claim 1 wherein the mol ratio of zinc oxide to total chromium oxides is about 1:1.
 3. A zinc chromium chromate corrosion inhibiting pigment as defined in claim 2 wherein 25 to 65% of the total chromium is present in trivalent state.
 4. A zinc chromium chromate corrosion inhibiting pigment as defined in claim 2 wherein approximately 42% of the total chromium is present in trivalent state.
 5. A zinc chromium chromate corrosion inhibiting pigment as defined in claim 1 wherein 25 to 65% of the total chromium is present in trivalent state.
 6. The method of preparing a corrosion-inhibiting pigment powder comprising a complex of zinc and chromium chromate which method comprises interacting zinc oxide with a preformed complex of trivalent and hexavalent chromium, in aqueous solution, drying the obtained reaction product and thereafter grinding the same to a powder.
 7. The method as defined in claim 6 wherein said chromium chromate complex solution is one obtained by partially reducing chromium trioxide in aqueous solution with a water soluble oxidizable organic compound having an active hydroxyl, aldehyde or carboxyl group.
 8. The method as defined in claim 7 wherein said organic compound is formaldehyde.
 9. The method as defined in claim 7 wherein said organic compound is methanol.
 10. The method as defined in claim 7 wherein said organic compound is furfural. 